Handbag, schoolbag, sports shoes and cap.
PRODUCT INFORMATION
Gloss ink, good printability and excellent adhension to bag cloth.
APPLICATION INFORMATION
MESH
Monofilament mesh, 60T-120T. 80T is recommended.
STENCIL
Using organic solvent resistant emulsions.
SQUEEGEE
65-85 durometer solvent resistant blade, such as PU.
COVERAGE
30 square meters per kilogram under 80T mesh.
PRINTING
This ink should be thinned with thinner approximately 10-20% by
weight base on the climate condition.
Available solvent:
SU thinner.
783 (slow dry), 718/cycloheanone (medium dry) or 719 (fast dry).
When environment temperature is over 30or application on small
printing area, slow and medium thinner should be selected. When
environment temperature is below 20or application on large printing
area, medium and fast thinner should be selected. Always mix well
prior to each use.
DRYING
Drying by solvent evaporation. Surface dry needs 10-20 minutes,
complete dry allows at least 24 hours.
(Drying time depends on actual weather condition and thinner usage)
CURE
Force to dry with hot dryer below 100is allowed.
CLEARS/EXTENDERS/ADDITIVES/CATALYST
Matt promoter(2-10%), anti-oxidizer(2-3%), 9004(2-8%), 9005,
flexible additive(0.5-0.8%).
ADHESION TESTING
Adhesive tape test C use adhesive tape to stick on test surface and
rip off, no ink should come off from test areas obviously.
CLEAN UP
Using organic solvent to clear the stencil.
PRODUCT RANGE AND PACKAGE
All of the colors are available in 1KG, 5KG and 20KG containers.
CAUTION
If 9004 or 9005 was added, the printing process should be finished
not more than 8 hours. The stencils and blades should be thoroughly
cleaned before process breaking.
Mischoice of the thinner may cause ink status damage.
Its the printers responsibility to pretest the ink selected prior
to engaging in a production run. Allow at least 24 hours after test
printing to evaluate the suitability of the ink and its adhesion to
the surface. Before using, the printer shall determine the
suitability of the product for its intended use. |